WHEN Newsletter Q4 2013 - Brake Drums

WHEN — Q4 2013

2

Dayton Parts LLC

(continued from page 1)

Update #2314

Machine Balanced Drums – I get asked regularly if our HD drums are balanced. The short answer is very likely and the long answer is a bit longer (of course). If a heavy duty brake drum is cast properly and the tolerances held tight enough (very doable with the manufacturing processes available today) then the finished drum will be within the specifications to be called balanced . Sometimes this is referred to “as cast balanced”. Our HD1 drum is made this way. If that is the case and most quality as cast finished drums are within the specs to be called balanced then why offer a machine balanced drum? Because a machine balanced drum goes through an additional process to verify or guarantee that the drum is balanced. So then, do you need a machine balanced drum for every type of application? Not really. Inboard mount trailer drums on cast spoke wheels like our HD4 comes to mind. This is an application where using a machine balanced drum isn’t really going to gain you anything. Drive axle applications for our HD1 drum I would say it’s a good idea but on trailer axles where the majority of these drums are used it’s not necessary. Steer axles on the other hand, especially with the larger 16.5" drums, are where a machine balanced drum makes really good sense. This is why over the last year Dayton Parts has changed all of our popular steer axle drums to a machine balanced version and that’s all we stock for these applications. Still from time to time we get back a machine balanced drum for being “out of round”. How can that be? How can a drum that has been checked and verified to be balanced be out of balance? There are several things to consider here. Summary – In all fairness there are probably a few over the road, general freight vocations with no severe braking, where you could use a “value” drum without any noticeable ill effects. However, this is not the usual customer for the wd/service shop/spring shop servicing the aftermarket and definitely not a big enough portion of the aftermarket to utilize all of the “value” drums being sold today. I fully realize we all have customers that buy on price alone and nothing else matters much to them. Not a lot you can do there. People believe what they choose to believe. You can talk “till the cows come home” and it probably won’t make any difference. However taking the time to explain to those who will listen that a “value” drum isn’t going to hold up for their application and why it won’t will go a long way in building a long term relationship with those customers. Now on to the next subject - Issue #1 - In a drum brake assembly, the hub/drum transfers the brake force from the foundation brake to the wheels/tires which in turn transfer it to the road and the vehicle slows down. Every time the brakes are applied the forward motion of the vehicle is changed into heat (energy is neither created nor destroyed but merely changes form). The brake drum absorbs this heat and dissipates it into the atmosphere. While the brake drum is absorbing all this heat it is also expanding or “growing” but there is a limit to how much heat a drum can absorb and dissipate. If the drum temperature rises above its ability to absorb and dissipate the heat accordingly it will start to “over expand” and separate. These points of separation are commonly referred to as heat checks. A brake drum with less material (weight) will reach the point of heat checking sooner simply because there is less mass to dissipate the heat. A lower quality material will take less time because it will expand at a faster rate. Once a drum has heat checks, they remain for the duration of its service life. When the brakes are applied, heat checks are like dragging a file across the friction material. Issue #2 - As the brake temperature rises, so does the temperature of the friction material. The base ingredients in most friction material have the ability to reflect away a lot of heat (into the drum of course which is basically a heat sink). However, when the surface temperature (the top few thousandths of an inch) of the friction material spikes above 650 degrees the resin loses its bonding capabilities and friction material is lost a few thousandths at a time. It doesn’t matter what the base ingredients are once the surface temperature gets above 650 degrees, the resin can no longer hold them together. A brake drum with a lower weight/lesser quality material that can’t absorb the amount of heat the brake is generating and dissipate it sufficiently will have the surface temperature of the friction material spike above 650 degrees more often and stay there longer. A higher quality friction material will still have better, more consistent braking characteristics but the service life will be diminished thanks to the “value” drum. A lower grade friction material will have its service life shortened even more because it’s less able to reflect away heat. What a “value”, eh? Also, what usually determines when a brake job needs to be done? The condition of the brake drum or the thickness of the brake lining?

continued on page 3

Made with