GB06 Low Viscosity CA TDS 2017

GB06

TECHNICAL DATA SHEET FOR GB06

TYPICAL APPLICATIONS

PRODUCT DESCRIPTION

GB06 is specially formulated for the bonding of plastics, rubbers, wood,metals andother common substrates.

GB06 is a low-mediumviscosity (40cPs)modified EthylCyanoacrylate adhesive.

Recommended for use on close-fitting parts and smooth, even surfaces.

GB06 is suitable for bonding a very wide range of materials, including some porous ones, where very fast curespeed is required.

PROPERTIES OF UNCURED MATERIAL

TYPICAL CURING PERFORMANCE Typical Speed:

Chemical type Appearance Specific Gravity Viscosity cPs 1 – range – typical value TensileStrength 2

Ethyl Clear 1.06

<15 seconds <10 seconds <5 seconds <3 seconds

Steel/steel ABS/ABS

Rubber/Rubber Wood (balsa)

34-44 40

(N/mm 2 ) 21

FixtureTime Full Cure Flash Point

(secs)

2-20

(hours) 24

16 14 12 10

(  C)

> 85

Shelf Life@5  C

(months) 12

Max Gap Fill

(mm)

0.10

20% 30% 40% 50% 60%

-50 to +80

Operating Temperature Range (  C)

1 ISO 3104/3105 2 ISO 6922

8 6 4 2 0

CURE SPEEDS VS. ENVIRONMENTAL CONDITIONS

Cyanoacrylates require surfacemoisture on the substrates in order to initiate the curing mechanism. The speed of cure is reduced in low-humidity conditions. Low temperatures will also reduce cure speed. All figures relating to cure speed are tested at 21 o C.

1 2 3 4 5 6 7 CURE VS. HUMIDITY

CURE SPEED VS. SUBSTRATE

The speed of cure of cyanoacrylates varies according to the substrates to be bonded. Acidic surfaces such as paper and leather will have longer cure times than most plastics and rubbers. Some plastics with very low surface energies, such as polyethylene,polypropyleneandTeflon ® require theuse of 77 Primer (See PC 77 TDS for further info).

CURE SPEED VS. ACTIVATOR

CURE SPEED VS. BOND GAP

PROCURE / REACT cyanoacrylates give best resultsonclosefittingparts.Theproductshould be applied in a very thin line in order to ensure rapid polymerisation and a strong bond. Excessive bond gaps will result in slower cure speeds. PROCURE / REACT cyanoacrylate activators may be used to greatly increase cure speeds (see PC780 and PC750 TDS for further info).

Activators 780 and 750 may be used in conjunction with cyanoacrylates where cure speed needs to be accelerated.

Cure speeds of less than 2 seconds can be obtained with most cyanoacrylates.

The use of an activator can reduce the final bond strength by up to 30%Testingon theparts tomeasure the effect is recommended.